Termékek üveg cast gyanta (2)

Syntech HAG Acryl Syntech HAG Acryl is a four-component resin that reacts to form an elastic and durable gel. The properties of Syntech HAG Acryl are: • Good general chemical resistance. • Does not contain acrylamide, methacrylamide, formaldehyde or solvents. • Not inflammable. • Excellent adhesion on mineral building materials such as concrete, cement and bricks. • The reaction speed can be adjusted from a few seconds to several minutes. • When the injected cracks dry out due to temperature or groundwater level fluctuations the gel does not crack easily. • The hardened gel has excellent durability in wet-dry cycles. Syntech HAG Acryl components are supplied ready to use. Create 2 mixes in separate plastic buckets. Prepare only the quantity to be used each time. Solution 1: Syntech HAG Acryl component A (25 kg resin) mixed with Syntech HAG Acryl component B (2.5 kg catalyst). Solution 2: Syntech HAG Acryl component C (2 packs of 0.625 kg) mixed with clean tap water. Attention: The amount of water must be equal in volume to solution 1. When mixing resin, always use a wooden or stainless steel spatula. The reaction time depends on the temperature of the material, the structure of the building and the possible amount of water present. Higher temperature will speed up the reaction time and lower temperature will slow it down. It is advisable to carry out an on-site test, before injection, to observe and define the reaction time. To change the reaction time, only adjust the amount of Syntech HAG Acryl component C. The amount of the other components remains the same. Use a two-component stainless steel pump (manual, electric or pneumatic). Check that the pump and equipment are clean and that there is no residue from previous injection work. The two mixtures are fed into the pump separately, but are mixed homogeneously at a volumetric ratio of 1:1 in the pump's mixing head, before being injected through the pump nozzle. Check the quality of the concrete, as injection involves pressure. Sealing and waterproofing of cracks and cavities in walls, floors, concrete constructions, underground structures, etc. It can be used in constructions that are not permanently in contact with water (fluctuating groundwater level). Injection of very fine cracks. Determine the type and size of packers based on your pump and injection type. If reinforcing steel is present, try to locate it and plan the drilling pattern so that the reinforcement is not drilled. Drill holes at an angle of approximately 45° or less and in the direction of the crack. Make sure the hole goes through the crack. The distance of the drilled holes depends on the width of the crack. Place the packer in the hole. Prepare the pump to start the injection. The injection pressure varies depending on the structure and size of the crack. Start the injection at the lowest point of the crack. Continue injecting until resin flows out of adjacent packer(s). This is necessary to achieve uniform distribution of the material. Stop pumping, unplug and move on to the next packer. Continue the procedure until the crack is completely filled. After the material has cured, the packers can be removed. Holes drilled can be covered with Repar Tix Speedy HP quick-setting mortar. Clean and rinse the pump equipment with water whenever there is a stoppage longer than 15 minutes and, after completing the injection, rinse with a sufficient amount of water. Make sure the pump is clean and stop only when clean water comes out of the pump. The consumption of the product depends on the size of the empty volume to be filled. Can 25 kg [A] - Plastic can 2.5 kg [B] - Canister 0.625 kg [C] - Canister 0.625 kg [D] - Kit: 1 Can 25 kg [A] + 1 Plastic can 2.5 kg [B] + 1 Canister 0.625 kg [C] + 1 Canister 0.625 kg [D]

Fluid Col Multi-purpose additive powder, to add to a suitable mixture of binders and aggregates, for the on-site production of mortars, grouts and concretes that are self-levelling, rheoplastic, controlled shrinkage or moderately expansionary, high mechanical strength, chemical and waterproofing. The physical-chemical action of Fluid Col is an interaction of positive contributions and modifications: drastic reduction of the A/C ratio, shrinkage-resistant action, superpozzolanic action and reaction of ultrafine fillers (MICROSIL 90), which transforms unstable, soluble, readily reactive calcium hydroxides into stable, insoluble, chemically and mechanically resistant hydrous calcium silicates. Preparation of mortars, grouts, rheofluid concretes, shrinkage-compensated or moderately expansionary, high mechanical, watertightness and chemical stability performance, for structural slubs, anchoring machines, road joints, etc. Add the product in a concrete mixer, mixer truck or mixer, together with the remaining anhydrous components of the mixture: cement and aggregates, any polypropylene and/or steel fibres, etc. The indicative dosage, depending on the type of conglomerate to be packaged and its purposes, varies between 12% and 15% of the weight of the cement. After a first mixing, add the mix water and mix thoroughly, until you obtain a homogeneous whole and free of lumps. The cement dosage must not be less than 350 kg/m³. Fluid Col is perfectly compatible with the addition of fibre d steel and/or polypropylene fibres READYMESH, for the preparation of conglomerates composite s, fibre reinforced. Add 10 - 15% of Fluid Col to the weight of the cement present in the mixture. Bag 25 kg - Pallet: 50 x (Bag 25 kg)